Browsing by Author "Mohammed, S."

Now showing 1 - 3 of 3

EFFECT OF PARTIAL REPLACEMENT OF FINE AGGREGATE WITH SAWDUST IN LIGHT WEIGHT CONCRETE PRODUCTION USING BIDA NATURAL STONE AS COARSE AGGREGATE
(3rd International Engineering Conference, Federal University of Technology, Minna, Nigeria, 2019) Alhaji, Bala; Abubakar, Mahmud; Yusuf, A.; Oritola, S. F.; Mohammed, S.; Kolo, D. N.
This study investigated the effect of sawdust as partial replacement for Fine Aggregate in light weight concrete production. Sawdust was used to replace Fine Aggregate from 0% to 40% in steps of 5%. 150 x 150 x 150mm concrete cubes were cast for each replacement level, the concrete was cured and the compressive strengths were determined at 7, 21 and 28days curing period respectively. Increase in percentage of sawdust in concrete led to a constant reduction in the compressive strength values with a corresponding reduction in weight. From the result obtained, 5% replacement of Fine Aggregate with sawdust gave a maximum compressive strength 13.11 N/mm2. It was however concluded that the optimum replacement level of 5% can be used as plain concrete for blinding works.
Effect of Partial Replacement of Fine Aggregate with Sawdust in Light Weight Concrete Production Using Bida Natural Stone as Coarse Aggregate
(Proceedings of the 3rd International Engineering Conference, Federal University of Technology Minna, Nigeria, 2019) Alhaji, B.; Abubakar, M.; Yusuf, A.; Oritola, S. F.; Mohammed, S.; Kolo D. N.
This study investigated the effect of sawdust as partial replacement for Fine Aggregate in light weight concrete production. Sawdust was used to replace Fine Aggregate from 0% to 40% in steps of 5%. 150 x 150 x 150mm concrete cubes were cast for each replacement level, the concrete was cured and the compressive strengths were determined at 7, 21 and 28days curing period respectively. Increase in percentage of sawdust in concrete stant reduction in the compressive strength values with a corresponding reduction in weight. From the result obtained, 5% replacement of Fine Aggregate with sawdust gave a maximum compressive strength 13.11 N/mm2. It was however concluded that the optimum replacement level of 5% can be used as plain concrete for blinding works.
PARTIAL REPLACEMENT OF FINE AGGREGATE WITH WASTE GLASS IN CONCRETE MADE FROM BIDA NATURAL AGGREGATE
(3rd International Engineering Conference (IEC 2019) Federal University of Technology, Minna, Nigeria, 2019) Alhaji, B.; Kolo, D. N.; Abubakar, Mahmud; Yusuf, A.; Abdullahi, A.; Mohammed, S.
This study reports the experimental investigation on the suitability of waste glass as partial replacement for fine aggregate in concrete made using Bida natural aggregates (BNA). Glass is widely used in our daily lives through manufactured products such as sheet glass, bottles, glassware, and vacuum tubing. It is an ideal material for recycling. The increasing awareness of glass recycling speeds up inspections on the use of waste glass with different forms in various fields. Mix ratio of 1:2:4 batched by weight with water – cement ratio of 0.55 was used. The percentage replacement varied from 0% to 40% at 5% intervals. Slump test was conducted to assess the workability of the fresh concrete. The compressive strengths and densities of cured concrete cubes of sizes 150mm x 150mm x 150mm were evaluated at 7, 21 and 28days. A total of 81 concrete cubes were cast and tested. It was observed that an increase in the percentage replacement of fine aggregate with waste glass reduces workability, density and compressive strength. The compressive strength and density vary with days of curing. The findings of this study indicated that the optimum replacement percentage of waste glass with conventional fine aggregate was 20%. However waste glass can effectively be used as fine aggregate replacement (up to 40%) without substantial change in concrete strength.