    Hygrothermal Effects of Partial Replacement of Coarse Aggregates with Palm Kernel Shell in Concrete Production
    (Nigeria Journal of Engineering and Applied Sciences, 2017-08-12) Abdullahi A.; Abubakar M.; Aminulai H. O; YUSUF, Abdulazeez; Alhaji B.
    Hygrothermal effects of partial replacement of coarse aggregates with Palm Kernel Shell (PKS) in concrete production were assessed. Preliminary tests were conducted on PKS to determine its suitability for use as aggregate in concrete production. Workability and Density of the fresh concrete were also determined. Cylinders of 100mm diameter by 50mm height were used to cast the concrete; these were cured for 28 days and tested for water absorption and sorptivity at different replacement levels of coarse aggregates with PKS. The sorptivity of concrete was found to increase with increase in PKS content, however, between 5-25% PKS content, lower sorptivity values than control were recorded. Water absorption of concrete also increased with increase in PKS content, PKS contents from 5-20% gave water absorptions below the control and at 25% replacement, a slightly higher value as compared to the control was recorded. From the results obtained, concrete with 5% PKS content was found to possess the best water absorption as well as sorptivity values. Such concrete adequately fits for use in areas where concrete water absorption and sorptivity are required to be kept at a very minimal level; such as in the construction of drainages and dams.
  • No Thumbnail Available
    Item
    Partial Replacement of Fine Aggregate with waste Glass in Concrete made from Bida Natural Aggregate
    (. Proceedings of the 3rd International Engineering Conference, Federal University of Technology Minna, Nigeria, 2019-02-05) Alhaji, B.; Kolo, D. N.; Abubakar M.; Yusuf A.; Abdullahi, A.; Shehu, M.
    This study reports the experimental investigation on the suitability of waste glass as partial replacement for fine aggregate in concrete made using Bida natural aggregates (BNA). Glass is widely used in our daily lives through manufactured products such as sheet glass, bottles, glassware, and vacuum tubing. It is an ideal material for recycling. The increasing awareness of glass recycling speeds up inspections on the use of waste glass with different forms in various fields. Mix ratio of 1:2:4 batched by weight with water cement ratio of 0.55 was used. The percentage replacement varied from 0% to 40% at 5% intervals. Slump test was conducted to assess the workability of the fresh concrete. The compressive strengths and densities of cured concrete cubes of sizes 150mm x 150mm x 150mm were evaluated at 7, 21 and 28days. A total of 81 concrete cubes were cast and tested. It was observed that an increase in the percentage replacement of fine aggregate with waste glass reduces workability, density and compressive strength. The compressive strength and density vary with days of curing. The findings of this study indicated that the optimum replacement percentage of waste glass with conventional fine aggregate was 20%. However waste glass can effectively be used as fine aggregate replacement (up to 40%) without substantial change in concrete strength.